The Development Body Texture For Stoneware Products Of Ban Plugrat Bangrakam District Phitsanulok

Main Article Content

วิมล ทองดอนกลิ้ง

Abstract

The research intend to develop research and stoneware clay with the following goals 1. Experiment
to find the right formula for Stoneware products. Ban Plugrat, Bang Rakam district of Phitsanulok 2. 10 samples
of clay pottery products through a new experimental model number 10 by firing temperature 1230 ° C in
atmospheric oxidation damage 3. Comparison with the original product. The trial is using a sampling method
by sampling using square triangle has formulated mixture of clay all 360 formulation according to the ratio of
random then the tried and tested by the trials of clay Stoneware. and the data obtained from the experiments
to be analyzed by looking up strength after the burning of the contraction. The water absorption Observe the
color of ground beef The fire-resistant and suitable for the coating of clay by molding. The analysis concluded
that the clay. Stoneware clay based mud rhino house number 10 samples Lampang kaolin and feldspar.
Sintered at 1230 °C in Oxidation atmosphere. Body can withstand all fire formulas. Ingredients and test results
of Stoneware Ban Plug Rad 10 samples of Lampang and Feldspar. All formulas in the experiment can be
molded into the product using the rotary pad. It has the following physical properties: After the incubation, it
was found that the postharvest shrinkage of Ban Plug Rad Clay was between 0.00 - 9.48% The postharvest
strength of Ban Plug Rad Clay Between 81.46 Kg / cm3 and 237.84 Kg / cm3, the water absorption of Ban Plug
Rad Clay was between 0.00 - 12.32. The fire resistance of Ban Plug Rad Clay was between 30% of rhinoceros,
30% of Lampang, and 40% of feldspar. colors of clay after firing of clay Ban Plugrat 10 samples sintered at
1230 °C showed that each formula is a color similar to the color of clay the color gray,cream,brown,cream,light
brown to dark brown And Auburn Color is the color of ferric oxide from clay which concluded that. During
the formulation of quality clay soil with a mixture of mud houses rhino 10 samples in quantities suitable for
production of stoneware pottery. The need for a cohesive clay and a mixture of kaolin production in Lampang
a material that has properties that make products A white and a mixture of feldspar is helping cause the glass
on clay too And experimental clay clay with a mixture of mud houses rhino products is the main material
damage only 3% from 15% due to distorted and caused a lot of blame on the product. Research in this clay
that is suited to the production of stoneware very seriously and the selection formula from the experimental
to the operator of 10 formulation of clay Ban Plugrat 1 formula at 19 clay Ban Plugrat 2 formulation that 19
clay Ban Plugrat 3 ingredient recipe first clay Ban Plugrat 4 formulated at five clay Ban Plugrat 5 ingredient
recipe 20 clay Ban Plugrat 6 formula at 26 clay Ban Plugrat 7 formulated the 21 clay Ban Plugrat 8 formulated
the 33 clay Ban Plugrat 9 formulation at 34 and clay Ban Plugrat 10 formulation that 10 results from trials
molded by forming blade is capable of forming any formula which satisfies the BangKeaw Ceramic.

Keywords

Article Details

Section
บทความวิจัย

References

โกมล รักษ์วงศ์. (ม.ป.ป.).การทำเนื้อดินปั้นสโตนแวร์สำหรับการขึ้นรูปด้วยวิธีหล่อ. กรุงเทพฯ : อุตสาหกรรมศิลป์ วิทยาลัยครูพระนคร.

งานวิจัยเตาเผาและเครื่องปั้นดินเผาเตาเผาแม่น้ำน้อยเพื่อสืบสารและอนุรักษ์ศิลปวัตถุโบราณของจังหวัดสิงห์บุรี. กรุงเทพฯ : สถาบันราชภัฏพระนคร, 2538 ก.

ดนัย อารยะพงษ์. (ม.ป.ป.). "การขึ้นรูปผลิตภัณฑ์โดยการหล่อแบบ," เอกสารประกอบการสัมมนาทางวิชาการเรื่อง เทคโนโลยีเซรามิกส์. ภาควิชาวัสดุศาสตร์ คณะวิทยาศาสตร์ จุฬาลงกรณ์มหาวิทยาลัย.

ปรีดา พิมพ์ขาวขำ. (2530). เคลือบเซรามิกส์. กรุงเทพฯ : อักษรเจริญทัศน์.

ประดุจฤดี สารสิทธิ์. (2549). การวิจัยเพื่อการบริหารงานอุตสาหกรรม. นครศรีธรรมราช: คณะเทคโนโลยีอุตสาหกรรม มหาวิทยาลัยราชภัฏนครศรีธรรมราช.

ไพจิตร อิ่งศิริวัฒน์. (2541). เนื้อดินเซรามิก. กรุงเทพฯ : โอเดียนสโตร์.

ไพจิตร อิ่งศิริวัฒน์. (2541). รวมสูตรเคลือบเซรามิกส์. กรุงเทพฯ : โอเดียนสโตร์.

อายุวัฒน์ สว่างผล. (2541). วัตถุดิบที่ใช้แพร่หลายในงานเซรามิกส์. กำแพงเพชร : สถาบันราชภัฏ-กำแพงเพชร.

องอาจ นฤภัยและคณะ, (ม.ป.ป). : 81. ปัญหาและการแก้ไขความเสียหายในผลิตภัณฑ์เซรามิก พิมพลักษณ์ กรุงเทพฯ : กรมส่งเสริมอุตสาหกรรม,