Main Article Content
In this study, a template synthesis was employed for preparing calcium hydroxide from industrial eggshell waste. Both effect of template chemicals e.g. ethanol, isopropanol, butanol and pentanol, and synthesis temperatures on properties of calcium hydroxide were systematically investigated. The results from N2 adsorption onto synthesized calcium hydroxide at -195 °C indicated that kinematic diameter of template alcohols played an important roles on specific surface area of synthesized calcium hydroxide. Synthesis of calcium hydroxide at room temperature using isopropanol as template exhibited high specific surface area of 47.96 m2/g, which was higher than conventional synthesized calcium hydroxide. In addition, synthesizing of calcium hydroxide and further activation at high temperature led to decrease of specific surface area of calcium hydroxide.
Each article is copyrighted © by its author(s) and is published under license from the author(s).
Kawashima A, Matsubara K, Honda K. Acceleration of catalytic activity of calcium oxide for biodiesel production, Bioresource Technology. 2009; 100(2): 696-700.
Kong L, Liu M, Diao Z. et al. Coupling template nanocasting and self-activation for fabrication of nanoporous carbon, Scientific Reports. 2016; 6, 1-9.
Ladhan S, Putkham AI, Chaiyachet Y. et al. Synthesis of High Surface Area of CaO from Industrial Eggshell Waste via Chemical Processes, Journal of Science and Technology Mahasarakham University: Special Issue Mahasarakham Research Conference. 2017; 13: 206-213.
Lesbani A, Tamba P, Mohadi R. et al. Preparation of calcium oxide from Achatina fulica as catalyst for production of biosiesel from waste cooking oil, Indonesian Journal of Chemistry. 2013; 13(2): 176-180.
Liu X, Piao X, Wang Y. et al. Calcium methoxide as a solid base catalyst for the transesterification of soybean oil to biodiesel with methanol, Fuel. 2008; 87(7): 1076-1082.
Pornchai T, Putkham AI, Putkham A. Effect of calcination time on physical and chemical properties of CaO-catalyst derived from industrial-eggshell wastes, Journal of Science and Technology Mahasarakham University. 2016; 35(6): 693-697.
Putkham AI, Putkham A. Synthesis and characteristics of Calcium oxide as a catalyst in biodiesel production, Naresuan University Journal: Science and Technology. 2014; 22(3): 29-46.
Rodriguez-Navarro C, Vettori I, Ruiz-Agudo E. Kinetics and Mechanism of Calcium Hydroxide Conversion into Calcium Alkoxides: Implications in Heritage Conservation Using Nanolimes, Langmuir. 2016; 32(20): 5183-5194.
Shin HG, Kim H, Kim YN. et al. Preparation and characterization of high surface area calcium hydroxide sorbent for SO2 removal, Current Applied Physics. 2009; 9(3): S276-S279.
Van der Perre S, Van Assche T, Bozbiyik B. et al. Adsorptive Characterization of the ZIF-68 Metal-Organic Framework: A Complex Structure with Amphiphilic Properties, Langmuir. 2014; 30(28): 8416-8424.
Watcharathamrongkul K, Jongsomjit B, Phisalaphong M. Calcium oxide based catalysts for ethanolysis of soybean oil, Songklanakarin Journal of Science and Technology. 2010; 32(6): 627-634.
Yoosuk B, Udomsap P, Puttasawat B. et al. Modification of calcite by hydration–dehydration method for heterogeneous biodiesel production process: The effects of water on properties and activity., Chemical Engineering Journal. 2010; 162(1): 135-141.
Zhu H, Wu Z, Chen Y. et al. Preparation of biodiesel catalyzed by solid super base of calcium oxide and its refining process, Chinese Journal of Catalysis. 2006; 27: 391-396.